ルリマットNo.10(1.8L) draft これらの工程を経ることで、描き味滑らか、呉須の濃度が濃くても焦げづらくなっております。

これらの工程を経ることで、描き味滑らか、呉須の濃度が濃くても焦げづらくなっております。

For over half a century

Glazing : Baume concentration 50° (soak for about 3 seconds)

even if it is applied under the same conditions as when it was first delivered

this clean water will decay and cause the glaze to crack when it is applied

ルリマットNo.10(1.8L) draft これらの工程を経ることで、描き味滑らか、呉須の濃度が濃くても焦げづらくなっております。[Firing conditions for sample plates] Clay components <br>For porcelain: Amakusa Senchu (SiO2 72. 04% Al2O3 18. 16% Fe2O3 0. 65% TiO2 0. 04% CaO 0. 49% MgO 0. 09% Na2O 0. 58% K2O 3. 00% Ig. Loss 4. 55%) Firing temperature : Reduction: 1280 Glazing : Baume concentration 50 (soak for about 3 seconds) [How to use] Soil type: porcelain, pottery Possible firing method: oxidation and reduction possible Appropriate firing temperature: 1230 1300 Baume